Rubbery laminate and composite hose

ABSTRACT

Composite laminates are disclosed which are designed to exhibit superior resistance to oil and to heat and which are comprised essentially of two different rubbery layers and a fibrous layer interposed therebetween. One rubber layer is formed from a rubber composition made up of highly hydrogenated acrylonitrile-butadiene rubber, an organic peroxide curing agent and magnesium oxide, and the other from a rubber composition of a rubber other than chlosulfonated polyethylene rubber. The fibrous layer is formed from an organic fiber treated with a dip coating of a specified composition. Also disclosed is a composite hose in which the rubbery layers and fibrous layer are assembled.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention is directed to composite laminates comprised of a rubbery layer formed from a rubber composition of a selected acrylonitrile copolymer and a fibrous layer formed from a selected organic fiber treated with a specified dip coating, both layers being bonded together into an integral structure. The invention further relates to composite hoses having such rubbery and fibrous layers assembled as constituent parts.

2. Description of the Prior Art

Rubber products such as hoses, tires, belts, rolls, shapes and the like have of late found application under oil-stained, elevated temperature and pressure conditions for prolonged periods of time. Fast deterioration of such product literally needs laborious maintenance and replacement and will in some instances lead to serious hazards.

A variety of rubbers are know to be resistant to oil and to heat at from 120° to 150° C. They include acrylonitrile-butadiene rubber (NBR), acryl rubber (ACM), ethylene-acryl rubber (AEM), ethylene-acryl-vinyl acetate rubber (ER), chlorosulfonated polyethylene rubber (CSM), chlorinated polyethylene rubber (CM) and the like and also modified NBR rubbers having their conjugated diene units hydrogenated. To meet the users' strict requirements in regard to heat resistance even at about 170° C., certain acrylonitrile copolymers have been proposed in which the conjugated diene units are hydrogenated at a greater degree.

In general, rubber compositions are broadly classifiable into two modes of vulcanization, one of which is sensitive to sulfur and the other to organic peroxide. Peroxide vulcanization is preferred to attain improved heat resistance. From the adhesion point of view, sulfur vulcanization is commonly accepted as many rubber products are usually built of rubber and fiber.

Highly hydrogenated acrylonitrile copolymers are necessarily subjected to peroxide vulcanization. This leaves the problem that such specific rubbers will not sufficiently bond to fibrous material, resulting in a composite laminate of poor structural strength. There has been still much to be desired in making the fullest use of the beneficial effects of those rubbers.

SUMMARY OF THE INVENTION

It has now been found that composite laminates of superior adhesion characteristics can be obtained by the use of acrylonitrile copolymers of high hydrogenation degrees combined with an organic fiber treated with a specific dip coating.

The present invention therefore seeks to provide a composite laminate which comprises two different rubbery layers of selected rubber compositions and a fibrous layer of a selected organic fiber interposed therebetween and which excels in resistance to oil and heat. Further, the invention seeks to provide a composite hose having two such layers incorporated respectively as a core and as a reinforcement.

The above and other objects and advantages of the invention will become better understood from the following description taken in conjunction with the accompanying drawings. Like numerals refer to like or corresponding parts throughout the several views.

According to one aspect of the invention there is provided a composite laminate comprising (a) a first rubbery layer formed from a rubber composition comprising 100 parts by weight of a copolymeric rubber having in the molecular chain an unsaturated nitrile unit in an amount of 10 to 45 percent by weight, a conjugated diene unit in an amount up to 5 percent by weight and either one or both of an ethylenically unsaturated unit other than the unsaturated nitrile unit and a hydrogenated conjugated diene unit, 0.2 to 15 parts by weight of an organic peroxide curing agent and 1 to 20 parts by weight of magnesium oxide, (b) a second rubbery layer formed from a rubber composition comprising a rubber other than chlorosulfonated polyethylene rubber and (c) a fibrous layer formed from an organic fiber treated with a dip coating consisting essentially of 100 parts by weight of a vinyl pyrridine-styrene-butadiene rubber latex, 0 to 100 parts by weight of a styrene-butadeiene rubber latex and a resorcinol-formalin precondensate, the fibrous layer being interposed between the first and second rubbery layers.

According to another aspect of the invention there is provided a composite hose comprising (a) an inner tube formed from a first rubber composition comprising 100 parts by weight of a copolymeric rubber having in the molecular chain an unsaturated nitrile unit in an amount of 10 to 45 percent by weight, a conjugated diene unit in an amount up to 5 percent by weight and either one or both of an ethylenically unsaturated unit other than the unsaturated nitrile unit and a hydrogenated conjugated diene, 0.2 to 15 parts by weight of an organic peroxide curing agent and 1 to 20 parts by weight of magnesium oxide, (b) an intermediate layer formed from a second rubber composition comprising a second rubber other than chlorosulfonated polyethylene rubber, (c) a cover formed from a third rubber composition comprising chlorosulfonated polyethylene rubber, (d) a first reinforcement formed from an organic fiber and treated with a dip coating consisting essentially of 100 parts by weight of a vinyl pyrridine-styrene-butadiene rubber latex, 0 to 100 parts by weight of a styrene-butadiene rubber latex and a resorcinol-formalin precondensate, the first reinforcement being interposed between the inner tube and the intermediate layer and (e) a second reinforcement formed from an organic fiber and treated with a dip coating consisting essentially of 100 parts by weight of at least one latex of acrylonitrile-butadiene rubber and a carboxyl-modified rubber thereof and 30 to 70 parts by weight of a precondensate of resorcinol and formalin in a mol ratio of 5:3 to 1:1, the second reinforcement being disposed between the intermediate layer and the cover.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a front elevational view of a composite laminate embodying the present invention.

FIG. 2 is a view similar to FIG. 1 but illustrative of a modified form of the laminate.

FIG. 3 is a segmental perspective view, partly broken, of a composite hose constructed in accordance with the invention.

DETAILED DESCRIPTION OF THE INVENTION

Four rubber compositions contemplated under the invention are those referred to simply as rubbers A to D and described later.

Rubber A comprises at least one copolymeric rubber (a), an organic peroxide curing agent (b) and magnesium oxide (c).

Component (a) is an acrylonitrile copolymer which is highly hydrogenic in nature and notably resistant to oil and to heat. This copolymer is made up of a nitrile unit (ACN), a double carbon linkage unit (--C═C--) and a saturated methylene unit (--C--C--); that is, the component is composed of 10 to 45% by weight of an unsaturated nitrile unit, 0 to 5% by weight of a conjugated diene unit and 50 to 90% by weight of an ethylenically unsaurated unit other than the unsaturated nitrile unit or a hydrogenated conjugated diene unit or both.

The nitrile unit (ACN) has the formula ##STR1## and should range in content from 10 to 45%. Smaller contents than 10% would lead to inadequate oil resistance, whereas greater contents than 45% would show a decline in cold resistance.

The carbon-carbon unit (--C═C--) is a conjugated diene unit of the formula --CH₂ --CH═CH--CH₂)_(n) and should be in a content of less than 5%. This is interpreted to mean that the majority of the double carbon linkage has been hydrogenated. The carbon-carbon unit if larger than 5% would make the final mix less resistant to elevated temperature at above 120° C. and less proof to degraded oil.

The saturated methylene unit (--C--C--) is a unit represented by the formula (CH₂ --CH₂)_(n) and should be in a content of 50 to 90%. Greater contents than 90%, hence less unsaturated nitrile unit, would develop too low a resistance to oil to warrant commercial application. Smaller contents than 50%, hence more unsaturated nitrile unit, would fail to improve cold resistance. Methylene unit contents not exceeding 50%, hence decreased nitrile unit and increased carbon-carbon unit, would result in a rubber mix of reduced resistance to elevated temperature at above 120° C. and to degraded oil.

Specific examples of component (a) include hydrogenated rubbers such as of acrylonitrile-butadiene rubber, acrylonitrile-isoprene rubber, acrylonitrile-butadiene-isoprene rubber, acrylonitrile-butadiene-methyl acrylate rubber, acrylonitrile-butadiene-acrylate rubber, acrylonitrile-ethylene-butadiene rubber, acrylonitrile-butyl acrylate-ethoxyethyl acrylate-vinyl chloroacetate rubber, acrylonitrile-butyl acrylate-ethoxyethyl acrylate-vinyl norbornene rubber and the like. These rubbers may be used alone or in combination when it is found necessary.

Organic peroxides useful as component (b) in the invention are not specifically restrictive. Preferred are those having a half life of 10 hours and a decomposition temperature of 80° C. or higher and inducing no excessive crosslinking at a given curing temperature. This component typically includes dialkyl peroxides such as dicumyl peroxide, 1,3-bis(t-butylperoxyisopropyl)benzene, n-butyl 4,4-di-t-butylperoxy valerianic acid and the like. Component (b) should be added in an amount of 0.2 to 15 parts in terms of net peroxide based on 100 parts of component (a). The peroxide if smaller than 0.2 part would not be sufficient to cure component (a) and if greater than 15 parts would leave its residues and thus cause objectionable aging while in curing.

Component (c), magnesium oxide (MgO), has a role to improve adhesion of component (a) to fibrous material. This component should range in amount from 1 to 20 parts and preferably from 2 to 20 parts per 100 parts of component (a). MgO if less than 1 part would not be effective for adhesion and if more than 20 parts would produce no better results.

Rubber A may be incorporated, where desired, with various other additives such as fillers, plasticizers, antioxidants and the like.

Rubber B is made up of a sulfur- or peroxide-vulcanizable rubber (d) other than chlorosulfonated polyethylene rubber. The component (d) may be selected for example from natural rubber (NR), polyisoprene rubber (IR), styrene-butadiene rubber (SBR), acrylonitrile-butadiene rubber (NBR), chloroprene rubber (CR), ethylene-propylenediene rubber (EPDM) and the like.

Rubber B may be admixed with accelerators, fillers, plasticizers, autioxidants and the like.

Rubber C is a composition predominantly of chlorosulfonated polyethylene rubber (e) of the formula ##STR2## where the contents of Cl and S are in the range of 24 to 43% by weight and 1.0 to 1.4% by weight, respectively. Component (e) is reputed for its resistance to weather, ozone and chemicals and further for its heat resistance and flame retardance. This rubber is vulcanized in the presence of a unique curing agent (f) selected from a metal oxide, an organic peroxide or an organic acid. Specific examples include metallic oxides such as magnesium oxide, lead oxide, lead tribasic maleate and the like, resinous acids such as organic peroxides, hydrogenated rosins, abietic acid and the like and organic fatty acids such as stearic acid, lauric acid and the like.

Accelerators (g) in actual use may conveniently be employed to facilitate vulcanization of component (e). In examples of component (g) are included (1) amines such as hexamethylenetetraamine and the like, (2) aldehyde-ammonias such as acetaldehyde-ammonia and the like, (3) aldehyde-amines such as reaction products of n-butyl aldehyde and aniline and the like, (4) guanidines such as diphenylguanidine, di-o-tollylguanidine and the like, (5) thiureas such as ethylenethiurea(2-mercaptoimidazoline), diethylthiurea, trimethylthiurea and the like of the formula ##STR3## (6) thiazoles such as mercaptobenzothiazole, dibenzothiazyl disulfide, 2-mercaptobenzothiazole and the like typified by benzothiazoles and represented by the formula ##STR4## where X is a hydrogen atom, a metal or an organic group, (7) sulfenamides such as N-cyclohexyl-2-benzothiazole sulfenamide, N-t-butyl-2-benzothiazole sulfenamide, N-oxydiethylene-2-benzothiazole sulfenamide, N,N-diisopropyl-2-benzothiazole sulfenamide and the like typified by N-substituted-2-benzothiazole sulfenamides and represented by the formulae ##STR5## (8) thiurams such as tetramethylthiuram monosulfide, tetramethylthiuram disulfide, tetraethylthiuram disulfide, tetrabutylthiuram disulfide, dipentamethylenethiuram tetrasulfide and the like which are derivatives of a compound derived by reaction of a secondary amine with carbon disulfide and represented by the formula ##STR6## where R and R' each are a hydrogen atom or an alkyl group, the two substituents may be joined to form a ring, and x is an integer of 1, 2 or 4, (9) dithiocarbamates such as zinc dimethyldithiocarbamate, zinc diethyldithiocarbamate, zinc di-n-butyldithiocarbamate and the like which are metal salts or amine compounds derived from dithiocarbamic acid or a reaction product of a secondary amine and carbon disulfide, and represented by the formula ##STR7## where R and R' each are an alkyl group, and X is a metal or an amine, and (10) xythantogenates such as sodium isopropylxythantogenate, zinc butylxythantogenate and the like that are reaction products of alcohols and carbon disulfide. Components (f) and (g) include those compounds of both acidic and basic types. Basic compounds of component (f) may be used singly or combined with two or more.

Rubber C may if necessary be combined with the same additives as above noted in connection with rubber A.

Rubber D comprises a sulfur-vulcanizable rubber (h), an organic sulfur-containing compound (i), a silica (j), a resorcinol donor (k) and a methylene donor (1).

Component (h) may by suitable choice be taken from NR, IR, SBR, NBR and like rubbers.

Component (i) acts to vulcanize component (i). Suitable compounds of this component may be selected from 6-R-2,4-dimercapto-1,3,5-triazines of the formula ##STR8## where R is a mercapto, alkoxy, mono- or di-alkylamino, mono- or di-cycloalkylamino, mono- or di-arylamino or N-alkyl-N'-arylmino group. Particularly preferred is 2,4,6-trimercapto-1,3,5-triazine.

As component (i) there may also be used sulfur donors commonly accepted in the art. Such donor is a compound capable of separating sulfur as active sulfur during curing and then discharging the same out of the reaction system. Specific examples include (1) thiuram disulfides of the formula ##STR9## where R and R' each are a hydrogen atom or an alkyl group, the two substituents being connectable for ring formation, such as tetramethylthiuram disulfide, tetraethylthiuram disulfide, dipentamethylenethiuram disulfide and the like, (2) thiuram tetrasulfides of the formula ##STR10## where R and R' each are a hydrogen atom or an alkyl group, and the two substituents may be connected together for ring formation, such as dipentamethylene thiuram tetrasulfide and the like and (3) morpholine derivatives such as 4,4'-dithiomorpholine, dimorpholine disulfide, 2-(4-morpholinodithio)benzothiazole and the like.

The amount of component (i) to be added should be in the range of 0.1 to 15 parts and preferably 0.5 to 10 parts per 100 parts of component (h). Amounts if less than 0.1 part would render a given rubber less curable and hence physically vulnerable and if more than 15 parts would lead to insufficient scorching and unstable processability.

Component (j), silica, acts as an adhesion improver. This component should be added in an amount of 1 to 100 parts and preferably 1 to 50 parts based on 100 parts of component (h). Silica if less than 1 part would not be effective in improving adhesion and if more than 100 parts would make the resulting rubber mix too viscous for practical purposes.

Component (k) is a resorcinol donor also for use in improving adhesion. Typical of the donor are resorcinol, precondensates of resorcinol and formalin and the like. The donor should range in amount from 0.5 to 20 parts and preferably from 1 to 10 parts per 100 parts of component (h). Departures from this range should be avoided to preclude a decline in bondability.

Component (l) is a methylene donor useful as an adhesion improver. Preferred are hexamethylenetetraamine and the like. This donor should be added in an amount of 0.1 to 10 parts and preferably 0.5 to 5 parts based on 100 parts of component (h). The methylene donor if less than 0.1 part would fail to give acceptable adhesiveness and if more than 10 parts would lead to inadequate scorching while in curing.

As are in rubbers A to C, rubber D may also be added with other additives such as accelerators, fillers, plasticizers, antioxidants and the like.

Rubber D is a blend of rubbers B and C. The blend ratio is optionally determinable dependent upon the quality requirements of the final product.

In the practice of the invention two different dip coatings hereunder called dip coatings A and B should be used.

Dip coating A is comprised of a vinyl pyrridine-styrene-butadiene rubber latex (m), a styrene-butadiene rubber latex (n) and a resorcinol-formalin precondensate (o). This coating has superior bondability to highly hydrogenated acrylonitrile copolymers.

Component (m) excels in flex cracking resistance and in elasticity and contains as a dispersion phase vinyl pyrridine-styrene-butadiene rubber of the formula ##STR11## where a vinyl pyridine unit of the formula ##STR12## may preferably be in a content of about 15% by weight and a styrene unit of the formula ##STR13## in the range of 15 to 22% by weight.

Component (n) is physically balanced and converted when dried into a film. This component contains as a dispersion phase styrene-butadiene rubber of the formula ##STR14##

As styrene-butadiene rubber there are generally classified into three types in terms of the styrene contents, say 15 to 40%, 40 to 70% and 70 to 90%, and also into hot and cold classes at a polymerization temperature of 40° to 50° C. and of 5° to 10° C. A cold class of 15 to 40% in styrene content is preferred taking bondability in view. Such rubbr is efficient as a dipping component because of its least susceptibility to viscosity buildup even with the rise in molecular weight or dispersion concentration.

Component (o) acts as a resorcinol donor.

Component (n) should be added in an amount up to 100 parts and preferably up to 50 parts per 100 parts of component (m). Greater amounts than 100 parts would the resulting fiber less adhesive to highly hydrogenated acrylonitrile copolymers.

The amount of component (o) is not specifically limitative but feasible in the range of 10 to 50 parts per 100 parts of component (m) plus component (n).

In dip coating A there may be incorporated various other additives such as stabilizers, viscosity modifiers, antioxidants and the like. It has been found that dip coating A is not sufficiently bondable to chlorosulfonated polyethylene rubber.

Dip coating B comprises an acrylonitrile-butadiene rubber latex (p) and/or a carboxyl-modified acrylonitrile-butadiene rubber latex (q) and a precondensate (r) of resorcinol and formalin in a mol ratio of 5:3 to 1:1.

Components (p) and (q) excel in resistance to oil and to solvent and also in bondability.

Component (l) contains an NBR rubber of the formula ##STR15## in which the content of the acrylonitrile unit of ##STR16## may preferably range from 15 to 45%. Contents exceeding 25% are preferred to further improve oil resistance and adhesion capability. The dispersion phase has an average particle size in the range of 0.05 to 0.18 μm.

Component (q) contains a carboxyl-modified NBR rubber of the formula ##STR17## The dispersion phase has an average particle size of 0.04 to 0.12 μm. This component is superior in chemical and mechanical stability to component (p) and crosslinkable in the absence of sulfur.

Component (r) is used as a resorcinol donor composed of a resorcinol-formalin precondensate. The two constituent compounds should be charged in a mol ratio of 5:3 to 1:1. The mol ratio has been found critical to adhesion to rubber and further to stability of dip coating B with time. To this end the amount of the resorcinol donor should be in the range of 30 to 70 parts and preferably 40 to 60 parts per 100 parts of component (p) and/or component (q). Improved adhesion and stability qualities are dominated by the use of component (r) in the specified range of 30 to 70 parts.

Various other additives may be incorporated in dip coating B, and they include for example stabilizers, viscosity modifiers, antioxidants and the like.

Organic fibers eligible for the invention are suitable as reinforcements usually in the form of braids. The fiber should be treated with the above specified coatings so as to attain enhanced bonding to rubber. Such fibrous material may be selected typically from nylons, polyesters, rayons, cottons, vinylons, aramids and the like.

In accordance with one preferred embodiment of the invention, there are typically provided two different types of composite laminates.

A first laminate essentially comprises a first rubbery layer formed from rubber A predominatly of a selected class of highly hydrogenated acrylonitrile-butadiene rubbers, a second rubbery layer formed from rubber B containing a rubber other than chlorosulfonated polyethylene rubber and a fibrous layer formed from a selected class of organic fibers and treated with dip coating A, the fibrous layer being interposed between the first and second rubbery layers. A second laminate is constructed with a layer of rubber A, a layer of rubber C and a layer of rubber B disposed therebetween, a first reinforcement treated with dip coating A and interposed between rubbers A and B and a second reinforcement dipped in dip coating B and located between rubbers B and C. Rubber B may be substituted for rubber D in the two laminates exemplarily illustrated.

The first and second laminates may be vulcanized in conventional manner for instance at 130° to 200° C. with the use of indirect airing, direct steaming or pressing. Curing lengths of time may vary with the curing temperature. Firm interlamination is attributed primarily to rubber-rubber adhesion, dip coating-organic fiber hydrogen bonding, fiber strand-dip coating anchorage and rubber-latex covulcanization. Importantly, a fibrous layer disposed in direct adjacency to chlorosulfonated polyethylene rubber should be treated with dip coating B.

Another preferred embodiment of the invention provides composite hoses embodying the structural features of the foregoing laminates. A first hose has an inner tube formed from rubber A, a reinforcing layer formed from an organic fibrous material dipped in dip coating A and a cover formed from rubber B. A second hose is comprised of an inner tube, a first reinforcement, an intermediate layer, a second reinforcement and a cover superposed in the order mentioned, the inner tube being built of rubber A, the intermediate layer of rubber B and the cover of rubber C. The first reinforcement is treated with dip coating A and the second one with dip coating B.

The hose of the invention may be produced for instance by core extrusion, fiber dipping, fiber braiding, cover extrusion, vulcanization, mandrel removal and hose finishing. Braiding may usually be effected after drying and heat setting of dipped fibers. Vulcanization may suitably be done for example by the modes of lead wrapping, indirect airing, direct steaming and pressing. Temperature conditions are usually at from 130° to 200° C., and time conditions are not specifically restrictive but rather dependent on the temperature.

The following examples are provided to further illustrate the invention. In all formulations the numerical figures are indicated in part by weight unless otherwise noted.

Different rubber mixes were prepared as shown in Tables 1, 2-1 and 2-2 and milled by a mixing roll at 60° C. for 15 minutes. Into the dip coatings enumerated in Tables 3 and 4 plain cloth and fibrous material of nylon-66 (1,890 d/1) were dipped respectively at 20° C. for 5 minutes, followed by drying at 120° C. for 2 minutes and by subsequent heat setting for 2 minutes. The coatings were matured overnight prior to use.

Group I: Examples 1-3 and Comparative Example 1

Various rubber mixes shown in Table 5 were formed by a laboratory roll into their respective sheets of 2.5 mm in thickness. Each of the sheets was laminated with one and the plain cloth as above dipped after which a rubber-fiber structure was provided.

A plain cloth 12 of 15 cm×10 cm was interposed between two rubbery layers 11, 11 of 15 cm×10 cm×2.5 mm as seen from FIG. 1. Cellophanes 18 were interlaced for attachment to a gripper and also for peeling with simplicity. The resulting laminate 10 was press-cured into an integral structure on a laboratory press at a surface pressure of 30 kgf/cm² and at 153° C. for 90 minutes. On disposition at room temperature for 24 hours the cured laminate was cut to a width of 2.54 cm after which a test sample was obtained. Peel strength was examined with the results in Table 5.

Measurement was made on a tensile tester at a speed of 50 mm/min as stipulated in JIS K-6301. Greater than 4 kgf/25 mm are graded as acceptably resistant to peeling. In Table 5 the symbol "o" denotes material fracture upon naked inspect in and "x" interfacial peel.

Group II: Examples 4-5 and Comparative Example 2

The procedure of Example 1 was followed except for the use of the rubber mixes and dipped fibers shown in Table 6 together with the results obtained.

Group III: Examples 6-14 and Comparative Examples 3-8

The procedure of Example 1 was followed except that the rubber mixes and dipped fibers of Tables 7-1 to 7-4 were used and that a test sample was structured as illustrated in FIG. 2 in which plain clothes 16, 17 of 15 cm×10 cm was held in interposed relation to three different rubbery layers 13, 14, 15 of 15 cm×10 cm×2.5 mm and with cellophanes 18, 18, interlaminated, thereby providing a rubber-fiber-rubber-fiber-rubber structure 10.

In these examples bondability was further evaluated by testing the peel strength and appearance between the layer 13 and the cloth 16, between the layer 14 and the cloth 16 and between the layer 15 and the cloth 17. The results obtained are shown in Tables 7-1 to 7-4.

Group IV: Examples 15-17 and Comparative Example 9

Different composite hoses H were produced as formulated in Table 8 and illustrated in FIG. 3.

An inner tube 21 was formed by extruding a given rubber mix onto a mandrel to an inside diameter of 9.5 mm and also to a thickness of 1.6 mm. Dipped fiber of nylon-66 was braided over the inner tube to thereby form a first reinforcement 22 on which was disposed as an intermediate layer 23 a rubber sheet obtained at a thickness of 0.3 mm on a laboratory roll, and a second reinforcement 24 was then braided. Subsequently, a cover 25 was disposed peripherally over the second reinforcement by extrusion of a selected rubber mix to an outside diameter of 19.0 mm.

The hose thus assembled, after being covered with a nylon wrapper, was steam-vulcanized at 160° C. for 90 minutes after which the wrapper was uncovered and the mandrel pulled out. Performance evaluation was made of the resulting test hose particularly in regard to durability at high temperature under the conditions given below and with the results shown in Table 8.

Rupture pressure was measured in accordance with JIS K-6349 7.3(3). Pressures of larger than 580 kgf/cm² are preferable.

Volume expansion was examined by a SAE J188 procedure. This quality is acceptable in the range of 6 to 8 cc/ft.

Bending strength at low temperature was adjudged by immersing the hose in a temperature-constant vessel at -40° C., followed by standing for 24 hours, and subsequently by bending the hose at a curvature of 80 mm. Failures such as break and peel were inspected.

Impact resistance was determined as stipulated in SAE J118, Type I both at 140° C. and at 160° C. Acceptable cycles of durability are not less than 250×10⁴ at 140° C. and more than 70×10⁴ at 160° C.

Group V: Examples 18-19 and Comparative Example 10

The procedure of Example 15 was followed except that a test hose was produced as formulated in Table 9. The results obtained are shown in the same table.

Group VI: Examples 20-23 and Comparative Examples 11-12

The procedure of Example 15 was followed except for the use of the formulation of Table 10.

Group I is taken to evaluate the effect of MgO contents in rubber mix A upon adhesion to the organic fiber treated with dip coating A. As is apparent from Examples 1-3 the larger content of MgO, the greater the adhesion is with material fracture. Omission of MgO invited insufficient adhesiveness, leading to interfacial peel, as evidenced by Comparative Example 1.

Group II demonstrates the effect of the composition of dip coating A upon adhesion of the dipped fiber to rubber mix A. Departures of vinyl pyrridine-styrene-butadiene rubber latex to styrene-butadiene rubber latex ratios from the specified range, Comparative Example 2, revealed inadequate bonding and hence interfacial peel.

Group III is directed to a rubber-fiber-rubber-fiber-rubber laminate. Examples 6-14 have been found satisfactory in respect of all the properties tested. Comparative Example 3 in which MgO was absent in rubber mix A was inadequate in bonding. Controls in which dip coatings A and B were outside the scope of the specified compositions were impossible of dipping due to gelation as is apparent from Comparative Examples 4-8.

Group IV is concerned with a hose constructed with an inner tube of rubber mix A, an intermediate layer of rubber mix B, a cover of rubber mix C and two reinforcements of fibrous materials dipped according to the invention. One fiber braided over the inner tube was treated with dip coating A, and the other contacted with the cover was dipped in dip coating B. The effect of MgO in rubber mix A has been examined on the hose performance. A control devoid of MgO, Comparative Example 9, was inadequate in impact resistance and hence bonding capability at high temperature although it was acceptable in rupture pressure, volume expansion and bending strength at low temperature. The specified contents of MgO are highly effective in improving impact resistance with a level of other properties comparable to the controls as is evident from Examples 15-17. The inventive hose has been proved sufficiently durable even at 160° C.

Groups V and VI test the criticality of dip coating B for application to a reinforcement disposed in contact with the cover. The inventive hose, Examples 18-19, are notably resistant to impact at high temperature with other qualities comparable to those in Comparative Example 10 in which the latex-resorcinol-formalin ratios were outside the specified range.

Various changes and modifications may be made in the above described embodiments as conceived by those skilled in the art within the scope of the appended claims.

                  TABLE 1                                                          ______________________________________                                         rubber mix   A-1     A-2       A-3   A-4                                       ______________________________________                                         polymer (HSN)                                                                               100     100       100   100                                       ACN: 33 wt %                                                                   C═ C: 1.3 wt %                                                             C-- C: 65.7 wt %                                                               SFR Asahi No. 50                                                                            95      95        95    95                                        MgO          --      2         5     10                                        ZnO          2       2         2     2                                         stearic acid 1       1         1     1                                         Vulkanox DDA 1.5     1.5       1.5   1.5                                       Vulkanox ZMB-2                                                                              1.5     1.5       1.5   1.5                                       WAX PE 520   1       1         1     1                                         TAIC         2       2         2     2                                         Witamol 218  7       7         7     7                                         Parkerdox 14/40                                                                             7.5     7.5       7.5   7.5                                       ______________________________________                                    

                  TABLE 2-1                                                        ______________________________________                                         rubber mix        B-1                                                          ______________________________________                                         Nipol 1042 (NBR)  100                                                          SRF Asahi No. 50  60                                                           Nipseal AQ        20                                                           ZnO               5                                                            stearic acid      1                                                            resorcinol        3                                                            ZINSNET F         2                                                            DOP               20                                                           sulfur            2                                                            Nocceller MSA-G   1                                                            Nocceller H       2                                                            ______________________________________                                    

                  TABLE 2-2                                                        ______________________________________                                         rubber mix        C-1                                                          ______________________________________                                         Hyperlon 40 (CSM) 100                                                          SRF Asahi No. 50  80                                                           AC polyethylene   3                                                            MgO               5                                                            Nocrac NBC        1                                                            DOP               20                                                           litharge Yellow No. 1                                                                            5                                                            Sunceller TRA     1.5                                                          ______________________________________                                    

                  TABLE 3                                                          ______________________________________                                         dip coating    D-1      D-2      D-3   D-4                                     ______________________________________                                         latex (L)      Nipol LX110       --                                                         Nipol 2518FS                                                      ratio (LX110/2518FS)                                                                          300/100  100/100  33/100                                                                                0/100                                  resorcinol(R)/formalin(F)                                                                     1/2      1/2      1/2   1/2                                     (mol ratio)                                                                    R + F/L (wt ratio)                                                                             20/100   20/100  20/100                                                                               20/100                                  ______________________________________                                    

                                      TABLE 4                                      __________________________________________________________________________     dip coating       E-1  E-2  E-3  E-4  E-5  E-6  E-7  E-8  E-9                  __________________________________________________________________________     latex (L)         Nipol 1571                                                   resorcinol(R)/formalin(F) (mol ratio)                                                            10/3 5/3  5/4  1/1  5/8  5/4  5/4  5/4  5/4                  R + F/L (wt ratio)                                                                                50/100                                                                              50/100                                                                              50/100                                                                              50/100                                                                              50/100                                                                              20/100                                                                              35/100                                                                              65/100                                                                              80/100              __________________________________________________________________________     Notes to Tables 1, 2-1, 2-2, 3 and 4                                           material  maker       chemical nature                                          SRF Asahi No. 50                                                                         Asahi Carbon                                                                               SRF carbon black                                         Vulkanox DDA                                                                             Byer        diphenylamine derivative                                 Vulkanox ZMB-2                                                                           Byer        4,5-methylmercaptobenzimidazole zinc salt                WAX PE 520                                                                               Hoechst     wax                                                      TAIC      Nippon Kasei                                                                               triallyl isocyanate                                      Witamol 218                                                                              Dynamit Nobel                                                                              trimellitate ester                                       Parkerdox 14/40                                                                          Kayaku Nulley                                                                              1,3-bis(t-butylperoxyisopropyl)benzene                                         (content: 40 wt %)                                       Hyperlon 40                                                                              Dupont      chlorosulfonated polyethylene                            Nocrac NBC                                                                               Ohuchi Shinko Kagaku                                                                       nickel dibutyldithiocarbamate                            DOP       Chisso Petrochemical                                                                       2-ethylhexyl phthalate                                   Sunceller TRA                                                                            Sanshin Kagaku                                                                             dipentamethylenethiuram tetrasulfide                     Nipol 1042                                                                               Nippon Zeon acrylonitrile-butadiene rubber                           Nipseal AQ                                                                               Nippon Silica                                                                              silicon dioxide                                          resorcinol                                                                               Sumitomo Chemical                                                                          resorcinol                                               ZISNET F  Sankyo Kasei                                                                               2,4,6-trimercapto-1,3,5-triazine                         Nocceller MSA-G                                                                          Ohuchi Shinko Kagaku                                                                       N-cyclohexyl-2-benzothiazyl sulfeneamide                 Nocceller H                                                                              Ohuchi Shinko Kagaku                                                                       hexamethylenetetraamine                                  Nipol 1571                                                                               Nippon Zeon carboxyl-modified acrylonitrile-butadiene                                      rubber latex (solids content: 40%)                       Nipol LX110                                                                              Nippon Zeon styrene-butadiene rubber latex                                                 (solids content: 41.0%)                                  Nipol 2518FS                                                                             Nippon Zeon vinyl pyrridine-styrene-butadiene rubber            

                  TABLE 5                                                          ______________________________________                                                      Compara-                                                                       tive    Examples                                                  run            Example 1 1       2     3                                       ______________________________________                                         rubber layer 11                                                                               A-1       A-2     A-3   A-4                                                    (HSN)     (HSN)   (HSN) (HSN)                                   peroxide curing agent                                                                         +         +       +     +                                       MgO            -         2       5     10                                      dip coating for cloth 12                                                                      D-3       D-3     D-3   D-3                                     peel strength (kgf/25 mm)                                                                     2.5       5.0     7.0   9.5                                     appearance     x         ∘                                                                          ∘                                                                        ∘                           ______________________________________                                          +: added                                                                       -: not added                                                             

                  TABLE 6                                                          ______________________________________                                                      Compara-                                                                       tive    Examples                                                  run            Example 2 4       3     5                                       ______________________________________                                         rubber layer 11                                                                               A-4       A-4     A-4   A-4                                                    (HSN)     (HSN)   (HSN) (HSN)                                   peroxide curing agent                                                                         +         +       +     +                                       MgO            10        10      10    10                                      dip coating for cloth 12                                                                      D-1       D-2     D-3   D-4                                     peel strength (kgf/25 mm)                                                                     2.7       5.3     9.5   9.8                                     appearance     x         ∘                                                                          ∘                                                                        ∘                           ______________________________________                                    

                  TABLE 7-1                                                        ______________________________________                                                      Compara-                                                                       tive    Example                                                   run            Example 3 6       7     8                                       ______________________________________                                         rubber layer 13                                                                               A-1       A-2     A-3   A-4                                                    (HSN)     (HSN)   (HSN) (HSN)                                   peroxide curing agent                                                                         +         +       +     +                                       MgO            -         2       5     10                                      dip coating for cloth 16                                                                      D-3       D-3     D-3   D-3                                     rubber layer 14                                                                               B-1       B-1     B-1   B-1                                                    (NBR)     (NBR)   (NBR) (NBR)                                   dip coating for cloth 17                                                                      E-3       E-3     E-3   E-3                                     rubber layer 15                                                                               B-1       B-1     B-1   B-1                                                    (CSM)     (CSM)   (CSM) (CSM)                                   layer 13 - cloth 16 peeling                                                                    2.5       5.0     7.0   9.5                                    peel strength (kgf/25 mm)                                                                     x         ∘                                                                          ∘                                                                        ∘                           appearance                                                                     layer 14 - cloth 16 peeling                                                                   11.0      11.0    11.0  11.0                                    peel strength (kgf/25 mm)                                                                     ∘                                                                            ∘                                                                          ∘                                                                        ∘                           appearance                                                                     layer 14 - cloth 17 peeling                                                                   10.5      10.5    10.5  10.5                                    peel strength (kgf/25 mm)                                                                     ∘                                                                            ∘                                                                          ∘                                                                        ∘                           appearance                                                                     layer 15 - cloth 17 peeling                                                                    9.2       9.2     9.2   9.2                                    peel strength (kgf/25 mm)                                                                     ∘                                                                            ∘                                                                          ∘                                                                        ∘                           appearance                                                                     adhesion       x         ∘                                                                          ∘                                                                        ∘                           ______________________________________                                    

                  TABLE 7-2                                                        ______________________________________                                                      Compara-                                                                       tive    Example                                                   run            Example 4 9       8     10                                      ______________________________________                                         rubber layer 13                                                                               A-4       A-4     A-4   A-4                                                    (HSN)     (HSN)   (HSN) (HSN)                                   peroxide curing agent                                                                         +         +       +     +                                       MgO            10        10      10    10                                      dip coating for cloth 16                                                                      D-1       D-2     D-3   D-4                                     rubber layer 14                                                                               B-1       B-1     B-1   B-1                                                    (NBR)     (NBR)   (NBR) (NBR)                                   dip coating for cloth 17                                                                      E-3       E-3     E-3   E-3                                     rubber layer 15                                                                               C-1       C-1     C-1   C-1                                                    (CSM)     (CSM)   (CSM) (CSM)                                   layer 13 - cloth 16 peeling                                                                   2.7       5.3     9.5   9.8                                     peel strength (kgf/25 mm)                                                                     x         ∘                                                                          ∘                                                                        ∘                           appearance                                                                     layer 14 - cloth 16 peeling                                                                   3.4       8.6     11.0  11.2                                    peel strength (kgf/25 mm)                                                                     x         ∘                                                                          ∘                                                                        ∘                           appearance                                                                     layer 14 - cloth 17 peeling                                                                   10.5      10.5    10.5  10.5                                    peel strength (kgf/25 mm)                                                                     ∘                                                                            ∘                                                                          ∘                                                                        ∘                           appearance                                                                     layer 15 - cloth 17 peeling                                                                   9.2       9.2     9.2   9.2                                     peel strength (kgf/25 mm)                                                                     ∘                                                                            ∘                                                                          ∘                                                                        ∘                           appearance                                                                     adhesion       x         ∘                                                                          ∘                                                                        ∘                           ______________________________________                                    

                                      TABLE 7-3                                    __________________________________________________________________________                  Comparative                                                                           Examples    Comparative                                    run          Example 5                                                                             11  8   12  Example 6                                      __________________________________________________________________________     rubber layer 13                                                                             A-4    A-4 A-4 A-4 A-4                                                         (HSN)  (HSN)                                                                              (HSN)                                                                              (HSN)                                                                              (HSN)                                          peroxide curing agent                                                                       +      +   +   +   +                                              MgO          10     10  10  10  10                                             dip coating for cloth 16                                                                    D-3    D-3 D-3 D-3 D-3                                            rubber layer 14                                                                             B-1    B-1 B-1 B-1 B-1                                                         (NBR)  (NBR)                                                                              (NBR)                                                                              (NBR)                                                                              (NBR)                                          dip coating for cloth 17                                                                    E-1    E-2 E-3 E-4 E-5                                            rubber layer 15                                                                             C-1    C-1 C-1 C-1 C-1                                                         (CSM)  (CSM)                                                                              (CSM)                                                                              (CSM)                                                                              (CSM)                                          layer 13 - cloth 16 peeling                                                                 9.5    9.5 9.5 9.5 --                                             peel strength (kgf/25 mm)                                                                   ∘                                                                         ∘                                                                      ∘                                                                      ∘                                                                      --                                             appearance                                                                     layer 14 - cloth 16 peeling                                                                 11.0   11.0                                                                               11.0                                                                               11.0                                                                               --                                             peel strength (kgf/25 mm)                                                                   ∘                                                                         ∘                                                                      ∘                                                                      ∘                                                                      --                                             appearance                                                                     layer 14 - cloth 17 peeling                                                                 3.4    9.3 10.5                                                                               8.8 *                                              peel strength (kgf/25 mm)                                                                   ∘                                                                         ∘                                                                      ∘                                                                      ∘                                                                      *                                              appearance                                                                     layer 15 - cloth 17 peeling                                                                 2.8    8.5 9.2 8.0 *                                              peel strength (kgf/25 mm)                                                                   x      ∘                                                                      ∘                                                                      ∘                                                                      *                                              appearance                                                                     adhesion     x      ∘                                                                      ∘                                                                      ∘                                                                      x                                              __________________________________________________________________________      *: impossible of determination due to gelation of dip coating            

                                      TABLE 7-4                                    __________________________________________________________________________                  Comparative                                                                           Examples    Comparative                                    run          Example 7                                                                             13  8   14  Example 8                                      __________________________________________________________________________     rubber layer 13                                                                             A-4    A-4 A-4 A-4 A-4                                                         (HSN)  (HSN)                                                                              (HSN)                                                                              (HSN)                                                                              (HSN)                                          peroxide curing agent                                                                       +      +   +   +   +                                              MgO          10     10  10  10  10                                             dip coating for cloth 16                                                                    D-3    D-3 D-3 D-3 D-3                                            rubber layer 14                                                                             B-1    B-1 B-1 B-1 B-1                                                         (NBR)  (NBR)                                                                              (NBR)                                                                              (NBR)                                                                              (NBR)                                          dip coating for cloth 17                                                                    E-6    E-7 E-3 E-8 E-9                                            rubber layer 15                                                                             C-1    C-1 C-1 C-1 C-1                                                         (CSM)  (CSM)                                                                              (CSM)                                                                              (CSM)                                                                              (CSM)                                          layer 13 - cloth 16 peeling                                                                 9.5    9.5 9.5 9.5 --                                             peel strength (kgf/25 mm)                                                                   ∘                                                                         ∘                                                                      ∘                                                                      ∘                                                                      --                                             appearance                                                                     layer 14 - cloth 16 peeling                                                                 11.0   11.0                                                                               11.0                                                                               11.0                                                                               --                                             peel strength (kgf/25 mm)                                                                   ∘                                                                         ∘                                                                      ∘                                                                      ∘                                                                      --                                             appearance                                                                     layer 14 - cloth 17 peeling                                                                 2.8    7.5 10.5                                                                               10.5                                                                               *                                              peel strength (kgf/25 mm)                                                                   ∘                                                                         ∘                                                                      ∘                                                                      ∘                                                                      *                                              appearance                                                                     layer 15 - cloth 17 peeling                                                                 2.5    6.5 9.2 9.3 *                                              peel strength (kgf/25 mm)                                                                   x      ∘                                                                      ∘                                                                      ∘                                                                      *                                              appearance                                                                     adhesion     x      ∘                                                                      ∘                                                                      ∘                                                                      x                                              __________________________________________________________________________

                  TABLE 8                                                          ______________________________________                                                    Comparative                                                                             Examples                                                   run          Example 9  15      16    17                                       ______________________________________                                         inner tube ruber                                                                            A-1        A-2     A-3   A-4                                                   (HSN)      (HSN)   (HSN) (HSN)                                    peroxide curing agent                                                                       +          +       +     +                                        MgO          -          2       5     10                                       dip coating for 1st                                                                         D-3        D-3     D-3   D-3                                      reinforcement                                                                  intermediate layer                                                                          B-1        B-1     B-1   B-1                                      rubber       (NBR)      (NBR)   (NBR) (NBR)                                    dip coating for 2nd                                                                         E-3        E-3     E-3   E-3                                      reinforcement                                                                  cover rubber C-1        C-1     C-1   C-1                                                   (CSM)      (CSM)   (CSM) (CSM)                                    rupture pressure                                                                            600-       590-    600-  600-                                     (kgf/cm.sup.2)                                                                              620        610     620   620                                      volume expansion                                                                            6-8        6-8     6-8   6-8                                      (cc/ft at 91 kgf/cm.sup.2)                                                     bending strength                                                                            ∘                                                                             ∘                                                                          ∘                                                                        ∘                            (-40° C.)                                                               impact   140° C.                                                                          80-       300-  320-  300-                                   resistance       160        350   350   350                                    (cycle × 10.sup.4)                                                                160° C.                                                                          20-       100-  100-  100-                                                    40         120   120   120                                    ______________________________________                                          ∘: acceptable                                                

                  TABLE 9                                                          ______________________________________                                                    Comparative                                                                             Example                                                    run          Example 10 18      17    19                                       ______________________________________                                         inner tube rubber                                                                           A-4        A-4     A-4   A-4                                                   (HSN)      (HSN)   (HSN) (HSN)                                    peroxide curing agent                                                                       +          +       +     +                                        MgO          10         10      10    10                                       dip coating for 1st                                                                         D-1        D-2     D-3   D-4                                      reinforcement                                                                  intermediate layer                                                                          B-1        B-1     B-1   B-1                                      rubber       (NBR)      (NBR)   (NBR) (BNR)                                    dip coating for 2nd                                                                         E-3        E-3     E-3   E-3                                      reinforcement                                                                  cover rubber C-1        C-1     C-1   C-1                                                   (CSM)      (CSM)   (CSM) (CSM)                                    rupture pressure                                                                            580-       600-    600-  600-                                     (kgf/cm.sup.2)                                                                              610        620     620   620                                      volume expansion                                                                            6-8        6-7     6-8   6-8                                      (cc/ft at 91 kgf/cm.sup.2)                                                     bending strength                                                                            ∘                                                                             ∘                                                                          ∘                                                                        ∘                            (-40° C.)                                                               impact   140° C.                                                                          60-       300-  300-  300-                                   rsistance        180        320   350   350                                    (cycle × 10.sup.4)                                                                160° C.                                                                          20-        90-  100-  100-                                                    40         120   120   120                                    ______________________________________                                    

                                      TABLE 10                                     __________________________________________________________________________                Comparative                                                                           Examples    Comparative                                                                           Examples                                  run        Example 11                                                                            25  27  21  Example 12                                                                            22  17  23                                __________________________________________________________________________     inner tube rubber                                                                         A-4    A-4 A-4 A-4 A-4    A-4 A-4 A-4                                          (HSN)  (HSN)                                                                              (HSN)                                                                              (HSN)                                                                              (HSN)  (HSN)                                                                              (HSN)                                                                              (HSN)                             peroxide curing agent                                                                     +      +   +   +   +      +   +   +                                 MgO        10     10  10  10  10     10  10  10                                dip coating for 1st                                                                       D-3    D-3 D-3 D-3 D-3    D-3 D-3 D-3                               reinforcement                                                                  intermediate layer                                                                        B-1    B-1 B-1 B-1 B-1    B-1 B-1 B-1                               rubber     (NBR)  (NBR)                                                                              (NBR)                                                                              (NBR)                                                                              (NBR)  (NBR)                                                                              (NBR)                                                                              (NBR)                             dip coating for 2nd                                                                       E-1    E-2 E-3 E-4 E-6    E-7 E-3 E-8                               reinforcement                                                                  cover rubber                                                                              C-1    C-1 C-1 C-1 C-1    C-1 C-1 C-1                                          (CSM)  (CSM)                                                                              (CSM)                                                                              (CSM)                                                                              (CSM)  (CSM)                                                                              (CSM)                                                                              (CSM)                             rupture pressure                                                                          580-   590-                                                                               600-                                                                               600-                                                                               590-   590-                                                                               600-                                                                               600-                              (kgf/cm.sup.2)                                                                            600    620 620 620 620    620 620 620                               volume expansion                                                                          7-8    6-8 6-8 6-7 7-8    6-8 6-8 6-7                               (cc/ft at 91 kgf/cm.sup.2)                                                     bending strength                                                                          ∘                                                                         ∘                                                                      ∘                                                                      ∘                                                                      ∘                                                                         ∘                                                                      ∘                                                                      ∘                     (-40° C.)                                                               impact 140° C.                                                                      80-   300-                                                                               300-                                                                               300-                                                                                90-   300-                                                                               300-                                                                               300-                              resistance 140    320 350 350 180    350 350 350                               (cycle × 10.sup.4)                                                              160° C.                                                                      30-   100-                                                                               100-                                                                               100-                                                                                30-   100-                                                                               100-                                                                               100-                                         50     120 120 120 60     120 120 120                               __________________________________________________________________________ 

What is claimed is:
 1. A composite laminate comprising:(a) a first rubbery layer formed from a rubber composition comprising 100 parts by weight of a copolymeric rubber having in the molecular chain an unsaturated nitrile unit in an amount of 10 to 45 percent by weight, a conjugated diene unit in an amount up to 5 percent by weight and either one or both of an ethylenically unsaturated unit other than said unsaturated nitrile unit and a hydrogenated conjugated diene unit in an amount of 50 to 90 percent by weight, 0.2 to 15 parts by weight of an organic peroxide curing agent and 1 to 20 parts by weight of magnesium oxide; and (b) a second rubbery layer formed from a rubber composition comprising a rubber other than chlorosulfonated polyethylene rubber; and (c) a fibrous layer formed from an organic fiber and interposed between said first and second rubbery layers, said fiber having been treated with a dip coating consisting essentially of 100 parts by weight of a vinyl pyridine-styrene-butadiene rubber latex, 0 to 100 parts by weight of a styrene-butadiene rubber latex and a resorcinol-formalin precondensate.
 2. The laminate of claim 1 further including a third rubbery layer and a second fibrous layer, said third rubbery layer being disposed over said second rubbery layer and formed from a chlorosulfonated polyethylene rubber composition, said second fibrous layer formed from an organic fiber and interposed between said second and third rubbery layers, said second fibrous layer having been treated with a dip coating consisting essentially of 100 parts by weight of at least one latex of acrylonitrile-butadiene rubber and a carboxyl-modified rubber thereof and 30 to 70 parts by weight of a precondensate of resorcinol and formalin in a mol ratio of 5:3 to 1:1.
 3. The laminate of claim 2 wherein said rubber composition for use in the second rubbery layer consists essentially of 100 parts by weight of a sulfur-vulcanizable rubber, 0.1 to 15 parts by weight of an organic sulfur-containing compound, a silica, a resorcinol donor and a methylene donor.
 4. The laminate of claim 1 wherein said copolymeric rubber is one hydrogenated member selected from the group consisting of acrylonitrile-butadiene rubber, acrylonitrile-isoprene rubber, acrylonitrile-butadiene-isoprene rubber, acrylonitrile-butadiene-methyl acrylate rubber, acrylonitrile-butadiene-acrylate rubber, acrylonitrile-ethylene-butadiene rubber, acrylonitrile-butyl acrylate-ethoxyethyl acrylate-vinyl chloroacetate rubber, acrylonitrile-butyl acrylate-ethoxyethyl acrylate-vinyl norbornene rubber and blends thereof.
 5. The laminate of claim 1 wherein said peroxide curing agent is selected from the group consisting of dicumyl peroxide, 1,2-bis(t-butylperoxyisopropyl)benzene and n-butyl 4,4-di-t-butylperoxy valerianic acid.
 6. The laminate of claim 1 wherein said organic fiber is selected from the group consisting of nylon, polyester, rayon, cotton, vinylon and aramid.
 7. The laminate of claim 3 wherein said sulfur-vulcanizable rubber is selected from the group consisting of natural rubber, polyisoprene rubber, styrene-butadiene rubber, acrylonitrile-butadiene rubber, chloroprene rubber and ethylene-propylene-diene rubber.
 8. The laminate of claim 3 wherein said sulfur-containing compound is represented by the formula 6-R-2,4-dimercapto-1,3,5-triazine where R is a mercapto, alkoxy, mono- or di-alkylamino, mono- or di-cycloalkylamino, mono- or di-arylamino or N-alkyl-N'-arylamine group.
 9. The laminate of claim 8 wherein said sulfur-containing compound is 2,4,6-trimercapto-1,3,5-triazine.
 10. The laminate of claim 3 wherein said resorcinol donor is resorcinol or a resorcinol-formalin precondensate.
 11. The laminate of claim 3 wherein said methylene donor is hexamethylenetetraamine.
 12. A composite hose comprising:(a) an inner tube formed from a rubber composition comprising 100 parts by weight of a copolymeric rubber having in the molecular chain an unsaturated nitrile unit in an amount of 10 to 45 percent by weight, a conjugated diene unit in an amount up to 5 percent by weight and either one or both of an ethylenically unsaturated nitrile unit and a hydrogenated conjugated diene unit in an amount of 50 to 90 percent by weight, 0.2 to 15 parts by weight of an organic peroxide curing agent and 1 to 20 parts by weight of magnesium oxide; (b) a reinforcing layer formed from an organic fiber and disposed over said inner tube, said fiber having been treated with a dip coating consisting essentially of 100 parts by weight of a vinyl pyrridine-styrene-butadiene rubber latex, 0 to 100 parts by weight of a styrene-butadiene rubber latex and a resorcinol-formalin precondensate; and (c) a cover laminated around said reinforcing layer.
 13. The hose of claim 12 wherein said cover is formed from a chlorosulfonated polyethylene rubber composition.
 14. The hose of claim 13 further including an intermediate rubbery layer and a second reinforcing layer interposed respectively between the first mentioned reinforcing layer and the cover, said intermediate rubbery layer being formed from a rubber composition comprising a rubber other than chlorosulfonated polyethylene rubber, said second reinforcing layer formed from an organic fiber treated with a dip coating consisting essentially 100 parts by weight of at least one latex of acrylonitrile-butadiene rubber and a carboxyl-modified rubber thereof and 30 to 70 parts by weight of a precondensate of resorcinol and formalin in a mol ratio of 5:3 to 1:1.
 15. The hose of claim 14 wherein said rubber composition for use in the intermediate rubbery layer consists essentially of 100 parts by weight of a sulfur-vulcanizable rubber, 0.1 to 15 parts by weight of an organic sulfur-containing compound, a silica, a resorcinol donor and a methylene donor. 